The purpose of a PEEK ceramic hybrid radial bearing is to reduce rotational friction and support loads. This is achieved by using two races to hold the balls and to spread the load through the balls. As the bearing race rotates it causes the balls to rotate. The ball provides for substantially less rolling resistance and coefficient of friction than if two flat surfaces were rotating.
PEEK is a semicrystalline thermoplastic with excellent mechanical and chemical resistance properties that are retained to high temperatures. The Young's modulus is 3.6 GPa and its tensile strength 90 to 100 MPa. PEEK has a glass transition temperature at around 143 °C (289 °F) and melts around 343 °C (662 °F). The thermal conductivity increases nearly linearly versus temperature between room temperature and solidus temperature. It is highly resistant to thermal degradation as well as attack by both organic and aqueous environments. It is attacked by halogens and strong Bronsted and Lewis acids as well as some halogenated compounds and aliphatic hydrocarbons at high temperatures. It dissolves completely in concentrated sulfuric acid at room temperature.
Properties of PEEK